Publication: Sintering effect on mechanical properties of composites of bovine hydroxyapatite (BHA) and Li2O
No Thumbnail Available
Date
2006
Authors
Oktar, Faik Nüzhet
Demirer, M. R.
Gündüz, Oğuzhan
Agathopoulos, S.
Peker, I.
Özyeğin, L. S.
Salman, Serdar
Journal Title
Journal ISSN
Volume Title
Publisher
Trans Tech Publications Ltd, Brandrain 6, Ch-8707 Zurich-Uetikon, Switzerland
Abstract
In this study, hydroxyapatite (HA) material, obtained from calcinated bovine bone (BHA), was mixed with 0.25, 0.50, 1.00, and 2.00 wt% Li2CO3. The pressed pellets were sintered at various sintering temperatures between 900 degrees C and 1300 degrees C. Measurements of compression strength, microhardness, and density, along with SEM observation and X-ray diffraction analysis were performed. The experimental results showed that the samples with 0.25 and 0.50% Li2CO3 reached a maximum of densification and the highest values of compression strength and microhardness were achieved after sintering at 1300 degrees C. The wetting effect of a Li2O-associated glassy phase was observed even from 900 degrees C.
Description
Keywords
bovine derived hydroxyapatite, lithium oxide, sintering, mechanical properties, Ceramics